Abstract
[Display omitted]
•AgNPs cross-linked within glass ionomer cement (GIC) matrices generated antibiofilm effects at the nanocomposite surface.•AgNP-containing GICs had higher compressive strengths and equivalent flexural strengths to unmodified GICs.
To develop a silver nanoparticle (AgNP) formulation for incorporation into glass ionomer cements (GICs) which minimises biofilm growth on restoration surfaces.
GICs, Fuji IX, Ketac Molar, and Riva Selfcure were modified with 6, 10 and 24 μg per GIC capsule of α-lipoic acid-capped AgNPs. Monoculture biofilms of Streptococcus mutans were cultured (72 h) on GIC specimens (n = 3) and biofilm accumulation was quantified using a viability stain with confocal laser scanning microscopy. Compression strength and flexural strength (CS & FS) were measured according to ISO 9917-1:2007 (n = 8, n = 25). GIC colour was measured at 0, 1, and 14 days following AgNP incorporation using a digital spectrophotometer. Silver release from AgNP-modified GIC specimens was monitored at 1, 3, 7 and 14 days using inductively coupled plasma-mass spectrometry.
AgNP-modified Fuji IX demonstrated the greatest reduction in biofilm accumulation, with 10 μg Ag/capsule inhibiting biofilm formation by 99%. Ketac Molar and Riva Selfcure required 24 μg Ag/capsule to achieve 78% biofilm reduction. AgNP-modified GICs demonstrated significantly higher CS and FS than sintered silver-containing GICs, and possessed equivalent or higher strength values when compared to unmodified GICs. The colour shades of AgNP-modified GICs were more comparable to VITA shades of non-modified GICs than were sintered silver-containing GICs. The silver (≥99.6%) remained within the GIC for at least two weeks following incorporation.
AgNP-modified GICs exhibited significant antibiofilm activity and retained mechanical properties equivalent or superior to non-modified GICs. AgNP-modified GICs could reduce bacterial colonisation on and around restorations thereby reducing restoration failure caused by secondary caries.