Abstract
To investigate the effect of decontamination procedures on the microshear bond strength (μSBS) of blood-contaminated resin-modified glass ionomer cement (RMGIC) bonded to resin composite (RC).OBJECTIVETo investigate the effect of decontamination procedures on the microshear bond strength (μSBS) of blood-contaminated resin-modified glass ionomer cement (RMGIC) bonded to resin composite (RC).Eighty RMGIC disc specimens were allocated into 5 groups (n=16). All groups except Group 2 were contaminated with blood. Group 1 had no decontamination procedure, Group 3 was decontaminated by rinsing, Group 4 was decontaminated by 34% phosphoric acid etching, and Group 5 was decontaminated by 5% sodium hypochlorite application. RMGIC specimens were subsequently bonded with RC using a universal adhesive in self-etch mode. μSBS tests were conducted using a universal testing machine at a crosshead speed of 1 mm/min. Failure mode analysis was conducted on RMGIC fracture surfaces under a scanning electron microscope.METHODSEighty RMGIC disc specimens were allocated into 5 groups (n=16). All groups except Group 2 were contaminated with blood. Group 1 had no decontamination procedure, Group 3 was decontaminated by rinsing, Group 4 was decontaminated by 34% phosphoric acid etching, and Group 5 was decontaminated by 5% sodium hypochlorite application. RMGIC specimens were subsequently bonded with RC using a universal adhesive in self-etch mode. μSBS tests were conducted using a universal testing machine at a crosshead speed of 1 mm/min. Failure mode analysis was conducted on RMGIC fracture surfaces under a scanning electron microscope.μSBS results indicated that Group 4 had the highest mean μSBS value of 6.22 ± 2.14 MPa, while Group 1 had the lowest mean μSBS value of 3.53 ±1.67 MPa. Significant differences were observed in the μSBS of Group 2 with no contamination (p=0.023) and Group 4 with decontamination by phosphoric acid-etching (p=0.003) when compared to Group 1 with blood contamination. No statistically significant differences (p>0.05) were observed between all other groups' μSBS. For all groups, the predominant mode of failure was adhesive failure between the RMGIC-RC interface, with a few mixed failures in RMGIC for Groups 2-5.RESULTSμSBS results indicated that Group 4 had the highest mean μSBS value of 6.22 ± 2.14 MPa, while Group 1 had the lowest mean μSBS value of 3.53 ±1.67 MPa. Significant differences were observed in the μSBS of Group 2 with no contamination (p=0.023) and Group 4 with decontamination by phosphoric acid-etching (p=0.003) when compared to Group 1 with blood contamination. No statistically significant differences (p>0.05) were observed between all other groups' μSBS. For all groups, the predominant mode of failure was adhesive failure between the RMGIC-RC interface, with a few mixed failures in RMGIC for Groups 2-5.Blood contamination before adhesive application significantly reduced the μSBS between RMGIC and RC. Phosphoric acid etching was the most effective blood decontamination procedure to improve the μSBS.CONCLUSIONSBlood contamination before adhesive application significantly reduced the μSBS between RMGIC and RC. Phosphoric acid etching was the most effective blood decontamination procedure to improve the μSBS.