Abstract
Denture stomatitis can pose serious health risks, especially to older people. Chemical denture cleaning agents must be effective, yet not adversely affect the longevity of removable dentures. Ready-to-use (RTU) neutral pH electrolyzed oxidizing water (EOW) is an effective biocide against Candida albicans biofilms on denture resins, but the effects of daily disinfection with EOW on the physical and mechanical properties of resins have not been established.
The purpose of this in vitro study was to investigate the effects of simulated long-term exposure to RTU EOW on the color, surface characteristics, and flexural strength of denture base resins.
Heat-polymerized (HP), 3D printed (3D) and computer-aided design and computer-aided manufacture (CAD-CAM)-milled (CC) denture resin specimens (square: 20×20×3.3 mm; beam: 64×10×3.3 mm) were immersed in tap water (TW), RTU EOW (Neutral Anolyte ANK; Envirolyte; EOW), or a commercial denture cleaning tablet solution (Polident 3-Minute; Glaxo SmithKline; PD), mimicking a 5-minute once daily disinfection routine performed up to 3.0 years. Color and surface roughness were recorded (n=3, squares), and changes in color (∆E00) and surface roughness (∆Ra) were calculated. Flexural strength (n=12, beams) and surface hardness (n=18, beams) were measured with a universal testing machine. The fractured surfaces of specimens were examined by scanning electron microscopy and energy dispersive spectroscopy. Data were assessed by performing the Shapiro-Wilk or D′Agostino and Pearson normality tests. Two-way ANOVA or the Kruskal-Wallis test with a post hoc Tukey HSD or Dunn multiple comparisons (α=.05) was used for statistical analyses.
No significant changes were found in either color or surface roughness for HP, 3D, and CC resins after 1.5-year and 3.0-year immersion in any of the agents (P>.05). The surface hardness of 3D resins reduced by 14% with TW and by 23% with EOW and PD at 3.0 years. The flexural strengths of all 3 resins were unaffected by 3.0-year immersion (P>.05).
Simulated long-term immersion disinfection with RTU neutral pH EOW did not adversely affect the physical and mechanical properties of HP or CC denture resins.